SiO2微球模板制备多孔硅与其热电性能研究
-
1. 河北师范大学 物理科学与信息工程学院, 河北 石家庄 050024;
2. 河北省新型薄膜材料实验室, 河北 石家庄 050024;
3. 石家庄理工职业学院 基础部, 河北 石家庄 050028 -
DOI：10.13763/j.cnki.jhebnu.nse.2016.03.006
Preparation and Thermoelectric Property Study of Porous Silicon Covered SiO2 Nanospheres Template
摘要/Abstract
利用SiO2微球模板法腐蚀Si片, 发现不仅提高了腐蚀速率, 而且孔洞更加均匀, 孔隙率和有序性有所提高.对所制备的多孔硅进行性能测试结果表明, 随腐蚀时间增加热导率降低.与相同时间无模板直接化学腐蚀多孔硅相比, SiO2微球模板法得到的多孔硅有更低的热导率.将多孔硅腐蚀时间75min与腐蚀时间90min进行比较, 样品的激活能由100.49meV增加到174.19meV, 电阻率略有上升.
The silicon that covered SiO2 nanospheres template was etched through the electrochemical corrosion method.The obtained samples with relatively homogeneous and ordered pores,and the corrosion rate is faster and porosity is higher than that without covered SiO2 template.The property of thermal conductivity was measured and analysised.The thermal conductivity is obviously decreased with the increasing of etching time.The thermal conductivity of the obtained samples is lower than that without covered SiO2 template.A comparison of the two samples of etching 75min and 90min by using the template indicates that the thermal activation energy increases from 100.49meV to 174.19meV,which makes the resistivity of the sample increase slightly.
关键词
参考文献 15
- [1] IOFFE A F.Semiconductor Thermoelements and Thermoelectric Cooling[M].London:Infosearch,1959:10.
- [2] WANG Xing,WU Ying,LIU Xiaowei,et al.A Template-based Method for Preparing Ordered Porous Silicon[J].J Porous Mater,2015,22(6):1431-1435.doi:10.1007/s10934-015-0023-9
- [3] XIE Kewen,WANG Xiaohong,CHEN Jing,et al.Investigation of Selectively Forming Porous Silicon Used in MEMS[J].Chinese Journal of Semiconductors,2002,23(6):668-671.doi:0253-4177(2002)06-0668-05
- [4] CHRISTOPHERSEN M,CARSTENSEN J,FÖLL H.Pore Formation Mechanisms for the Si-HF System[J].Mater Sci Eng B,2000,69(1):23-28.doi:10.1016/S0921-5107(99)00287-1
- [5] STÖBER W,FRINK A.Controlled Growth of Monodisperse Silica Spheres in the Micron Size[J].Colloid and Interface Science,1968,26(1):62-69.doi:10.1016/0021-9797(68)90272-5
- [6] FUJIKAWA R,BARYSHEV A V,NISHIMURA K,et al.Optical Study on Opaline Thin Films Grown by Vertical Deposition[J].Journal of Porous Materials,2006,13(3/4):287-290.doi:10.1007/s10934-006-8018-1
- [7] HU Xiaoyong,LIU Yuanhao,CHENG Bingying,et al.Fabrication of High Quality Three-dimensional Photonic Crystals[J].Chin Phys Lett,2004,21(7):1289-1291.doi:10.1088/0256-307X/21/7/029
- [8] KUAI Sulan,HU Xingfang,HACHE A,et al.High-quality Colloidal Photonic Crystals Obtained by Optimizing Growth Parameters in a Vertical Deposition Technique[J].Journal of Crystal Growth,2004,267(2):317-324.doi:10.1016/j.jcrysgro.2004.03.015
- [9] GOLDENBERG L M,WAGNER J,STUMPE J,et al.Ordered Arrays of Large Latex Particles Organized by Vertical Deposition[J].Langmuir,2002,18(8):3319-3323.doi:10.1021/la015659c
- [10] PENG Kuiqing,WU Yin,FANG Hui, et al.Uniform,Axial-orientation Alignment of One-dimensional Single-crystal Silicon Nanostructure Arrays[J].Angew Chem Int Ed,2005,44(18):2737-2742.doi:10.1002/anie.200462995
- [11] ZHANG Ting,WU Shaolong,ZHENG Ruiting,et al.Significant Reduction of Thermal Conductivity in Silicon Nanowire Arrays[J].Nanotechnology,2013,24(50):505718-1-505718-8.doi:10.1088/0022-3727/44/17/174034
- [12] YANG Lina,YANG Nuo,LI Baowen.Extreme Low Thermal Conductivity in Nanoscale 3D Si Phononic Crystal with Spherical Pore[J].Nano Lett,2014,14(4):1734-1738.doi:10.1088/0957-4484/24/50/505718
- [13] PETERMANN N,NIKLAS S,SCHIERNING G,et al.Plasma Synthesis of Nanostructures for Improved Thermoelectric Properties[J].J Phys D:Appl Phys,2011,44(17):174034-1-174034-9.doi:10.1021/nl403750s
- [14] SCHIERNING G.Silicon Nanostructures for Thermoelectric Devices:A Review of the Current State of the Art[J].Phys Status Solidi A,2014,211(6):1235-1249.doi:10.1002/pssa.201300408
- [15] MOTT N F.Condiction on Nan-crystalline Materials[J]. Philos Mag,1969,160(19):835-852.doi:10.1080/14786436908216358